The following specifications pertain to testing listed among other services that METL provides.
Taber Abrasion Specifications
ASTM, Military, ISO and more
Abrasion Resistance
ASTM B117
Standard Practice for Operating Salt Spray (Fog) Apparatus
Applies To
Salt Spray Corrosion Testing
ASTM G47
Standard Test Method for Determining Susceptibility to Stress-Corrosion Cracking of 2XXX and 7XXX Aluminum Alloy Products
Applies To
Stress Corrosion Testing
ASTM G64
Standard Classification of Resistance to Stress-Corrosion Cracking of Heat-Treatable Aluminum Alloys
Applies To
Stress Corrosion Testing
ASTM B678
Standard Test Method for Solderability of Metallic-Coated Products
Applies To
Solderability
ASTM C633
Standard Test Method for Adhesion or Cohesion Strength of Thermal Spray Coatings
Applies To
Thermal Barrier Coating Strength
ASTM B571
Standard Practice for Qualitative Adhesion Testing of Metallic Coatings
Applies To
Coating Adhesion
ASTM B137
Standard Test Method for Measurement of Coating Mass Per Unit Area on Anodically Coated Aluminum
Applies To
Coating Weight
MIL-A-8625
Anodic Coatings For Aluminum and Aluminum Alloys
Applies To
Taber Abrasion, Coating Weight
MIL-STD-202 Method 208
Solderability
Applies To
Solderability
MIL-DTL-53072
Chemical Agent Resistant Coating (CARC) System Application Procedures and Quality Control Inspection
Applies To
Taber Abrasion, Coating Weight
MIL-C-5541
Chemical Conversion Coatings on Aluminum and Aluminum Alloys
Applies To
Coating Weight
AMS 2772
Heat Treatment of Aluminum Alloy Raw Materials
Applies To
Electrical Conductivity